    Characterization of Ibere clay for the production of electrical porcelain pin insulators
    (International Research Journal Publishers, 2014-06) Onuoha, C.; Ovri, J. E. O.; Mark, U.
    The characterization of Ibere clay for the production of porcelain pin insulators was carried out for both the locally made porcelains and the standard. Test samples were made by varying the compositions of feldspar and quartz needed to form a mouldable plastic body with the clay. The following properties were determined: electrical resistivity, apparent porosity, water absorption, bulk density and linear shrinkage. Results obtained showed that apparent porosity, water absorption and electrical resistivity increased with increase in the composition of the non-plastic materials (feldspar and quartz) while bulk density and linear shrinkage decreased with increase in non-plastic materials. The chemical composition of the clay (43.94%SiO2, 26.54%Al2O3) compares well with previous works (40-60%Si2O, 25-45%l2O3) for the production of ceramic refractories. Linear shrinkage (8.33-9.68%), apparent porosity (10.81-17.30%) and water absorption (5.4110.84%) are in conformity with standards (7-10%, 16.45% and 8.20% respectively). Electrical resistivities recorded (0.79-1.39 x 107Ω-m) are in agreement with results obtained for standard (0.45 x 107Ω-m). These results are obtained in samples containing 50-70% clay, 20-30% feldspar and 10-20% quartz. It is therefore concluded that imported porcelains used by Power Holding Company of Nigeria (PHCN) can be replaced with porcelains made from Ibere clay.
  • Thumbnail Image
    ItemOpen Access
    Characterization of some Nigerian local clays for electrical porcelain applications
    (American Institute of Science, 2015) Ovri, J. E. O.; Onuoha, C.
    Clays from Ibere and Awo-omama were characterized for electrical porcelain application. Test samples were made by varying the compositions of feldspar and quartz required to form mouldable plastic bodies with each clay. The following properties were determined: electrical resistivity, apparent porosity, water absorption and linear shrinkage. This characterization was carried out for both the locally made porcelains and the Power Holding Company of Nigeria (PHCN) (standard) porcelain. Results obtained showed that, for both clays, apparent porosity, water absorption and electrical resistivity increased with increase in the composition of the non-plastic materials (feldspar and quartz) while linear shrinkage decrease with increase in non-plastic materials. Also, for both clays, samples containing 50-70% clays, 20-30% feldspar and 10-20% quartz were found to yield results that compared well with results found in the literature as well as results obtained for PHCN (Standard) porcelain. It is therefore concluded that both clays are suitable for electrical porcelain application